Home > Produkt-Liste > Extrudiertes Aluminiumprofil > Aluminium-Blech- & Platten-Auflage, kundenspezifische Aluminium-Blechteile

Aluminium-Blech- & Platten-Auflage, kundenspezifische Aluminium-Blechteile

Produktivität: 
800000ton Per Year
Ort Von Zukunft: 
China
Versorgungsmaterial-Fähigkeit: 
800000ton Per Year
Zertifikate : 
ASTM, GB/T

Basisinformation

Modell:  6061, 6082

Produktbeschreibung

Modell Nr .: 6061, 6082 Anwendung: Transport Werkzeuge Grade: 6000 Serie Technik: Roll Temper: T3 - T8 Marke: BAODI HS Code: 76061250 Typ: Aluminium Bleche Form: Rechteckige Oberflächenbehandlung: Quench Legierung: Alloy Zertifizierung: ASTM, GB / T Ursprung: China Unsere Firma produzieren Aluminiumblech und Platte 6061-T6,6082-T, mehr als 3000tons Lager, keine Mindestbestellungen, Standard size.Cut an Größe für Sie.Aluminum Blatt hat sehr gute maschinell machbar.Pls sehen die Details:
Specification Name: 6000 series Aluminum Sheet
Alloy: 6061, 6082, 6063 etc.
Temper: O, H112, T4, T6, T651 etc.
Thickness: 6-200mm
Width: Up to 1500mm
Surface treatment: mill finished, Print marks
Feature Machinability: In the harder T 4 and T6 tempers it is good. It is notably less easy to machine in the annealed temper.
FormingEasily cold worked and formed in the annealed condition. Stamping, bending, spinning, deep drawing are all readily accomplished using standard methods.
Welding: It has very good welding characteristics and may be welded by all of the common welding techniques.
Heat TreatmentSolution heat treat at 990 F for adequate time to allow for thorough heating and then water quench. Precipitation hardening is done at 320 F for 18 hours and air cool, followed by 350 F for 8 hours and air cooling.
Forging: It is capable of being hot forged at temperatures in the range of 900 F to 750 F.
Hot WorkingHot working may be done in the temperature range of 700 F to 500 F.
Cold WorkingCold working in the O temper condition is readily performed. The alloy is notably less easy to cold form in the T 4 and T 6 tempers.
AnnealingAnnealing should be done at 775 F for 2 to 3 hours followed by controlled cooling at 50 f per hour down to 500 F, then air cool.
AgingThe aging precipitation heat treatment is done at 350 F for 8 hours followed by air cooling. This produces the T6 temper.
Application Commonly used in the manufacture of heavy-duty structures requiring good corrosion resistance, truck and marine components, railroad cars, furniture, tank fittings, general structural and high pressure applications, wire products, pipelines, various toolings etc.
 
Alloy Chemical Component %≤
Si Fe Cu Mn Mg Cr Ni Zn Ti others Al
single total
6061 0.4- 0.8 0.7 0.15-0.4 0.15 0.8- 1.2 0.04-0.35 \ 0.25 0.15 0.05 0.15 remainder
6082 0.7- 1.3 0.5 0.1 0.4- 1.0 0.6- 1.2 0.25 \ 0.2 0.1 0.05 0.15 remainder
6063 0.2-
0.6
0.35 0.1 0.1 0.45-0.9 0.1 \ 0.1 0.1 0.05 0.15 remainder
Contact Ms. Sunny Mao   Mobile:86-18660566415

Firmeneinführungen:
Aluminum Sheet&Plate Stock, Custom Aluminum Sheet Parts
Unsere Verpackung:
Aluminum Sheet&Plate Stock, Custom Aluminum Sheet Parts
Willkommen, um mich für weitere Informationen und Lösung zu kontaktieren.


Web: www.ytbaodi.com

Produktgruppe : Extrudiertes Aluminiumprofil

Mail an Lieferanten
  • *Fach:
  • Um:

  • *Nachrichten:
    Ihre Nachrichten muss zwischen 20-8000 Zeichen sein