Einfache Aluminiumlegierung Blatt 5052 H32 eloxierte Qualität in der Herstellung Metall und Legierung

Modell Nr .: 5052 H32 Anwendung: Dekorationen, Kühlkörper, Transport Werkzeuge, Tür & Fenster, Glas Wand Grade: 5000 Serie Technik: Rolling Temper: H34 Sample: Free Spezifikation: SGS, ROHS HS Code: 76061290 Typ: Aluminium Bleche Form: Rechteckige Oberflächenbehandlung: Mühle Finish Legierung: Legierung Zertifizierung: ASTM, JIS, GB / T Warenzeichen: Baodi Herkunft: China Aluminium Blech und Platte 5052 Größe:

Temper: H32, H34, H112, O
Dicke: 0 & Periode, 5-150mm
Dimension: Nach Kundenwunsch & Zeitraum;

Aluminiumblech und Platten chemische Zusammensetzung:

Aluminiumwaage
Chrom 0 & Periode; 15 - 0 & Periode; 35
Kupfer 0 & Periode 1 max
Magnesium 2 & Periode; 2 - 2 & Periode; 8
Mangan 0 & Periode 1 max
Verbleib jeder 0 & Zeitraum; 05 max
Rest Gesamt 0 & Zeitraum; 15 max
Silikon & plus; Eisen 0 & Periode 45 max
Zink 0 & Periode 1 max

Unsere Firma Lieferanten Schneid Service, können wir schneiden, um verschiedene Form und anpassen, um Ihre Größe und Zeitraum, wie Dreieck, Kreis, rechteckige Form etc & Zeitraum, und egal, was spezielle Größe ist ok für uns & Zeitraum;

Aluminum sheet and plate Specification	Name: 5000 series Aluminum Sheet
	Alloy: 5052, 5005, 5754, 5083 etc.
	Temper: O, H12, H22, H32, H14, H24, H26, H18, H112 etc.
	Thickness: 0.2-200mm
	Width: Up to 1800mm
	Length: up to 6000mm
	Surface treatment: mill finished, PVC coated, Print marks
Aluminum sheet and plate 5052 feature	Machinability: It has relatively fair machinability. It is easier to machine in the hard temper than as annealed and the quality of finish is better if machined in the hard condition. Oil lubricants should be used for machining, except that very light cuts may be done dry.
	Forming: It is readily formed at room temperature. Successive cold working decreases the formability.
	Heat Treatment: It cannot be hardened by means of heat treatment. It does harden due to cold working.
	Forging: It may be forged in the temperature range of 950 F down to 500 F
	Cold Working: The alloy cold works readily and may be formed by drawing or spinning. However the amount of cold work imparted by spinning makes intermediate annealing necessary.
	Annealing: Anneal at 650 F and air cool.
	Hardening: Hardens only from cold working.
Aluminum sheet and plate 5052 application	hydraulic tubes, kitchen cabinets, small boats, home freezers, milk crates, aircraft tube, fencing, small boats, gas lines, refrigerator panels, utensils, welded pressure vessels, marine, auto aircraft cryogenics, drilling rigs, TV towers, transportation equipment, missile components etc.
Alloy	Chemical Component %≤
	Si	Fe	Cu	Mn	Mg	Cr	Ni	Zn	Ti	others		Al
										single	total
5052	0.25	0.4	0.1	0.1	2.2-2.8	0.15-0.3	\	0.1	\	0.05	0.15	remainder
5005	0.3	0.7	0.2	0.2	0.5-1.1	0.1	\	0.25	\	0.05	0.15	remainder
5754	0.4	0.4	0.1	0.5	2.6-3.6	0.3	\	0.2	0.15	0.05	0.15	remainder
5083	0.4	0.4	0.1	0.4-1.0	4.0-4.9	0.05-0.25	\	0.25	0.15	0.05	0.15	remainder